The temporal evolution of the characteristic wavelength (lambda) and ordering range (xi) of self-organized nanodot patterns induced during Ar+ ion beam sputtering on Si(001) and Si(111) surfaces is studied by atomic force microscopy and grazing incidence x-ray diffraction. The patterns exhibit initial coarsening of lambda (up to 54-60 nm) and increase in xi (up to 400-500 nm) after which both features stabilize. The pattern formation is only weakly controlled by the crystallographic surface orientation, Si(111) surfaces showing a faster evolution into a proper stationary state. This trend is attributed to a higher sputtering rate at this orientation, as confirmed by theoretical simulations. (c) 2006 American Institute of Physics.
Palabras Clave: surfaces, erosion, dots
Índice de impacto JCR y cuartil WoS: 3.977 (2006); 3.791 - Q2 (2020)
Referencia DOI: 10.1063/1.2398916
Publicado en papel: Diciembre 2006.
Publicado on-line: Diciembre 2006.
R. Gago, L. Vázquez, O. Plantevin, T.H. Metzger, J. Munoz-Garcia, R. Cuerno, M. Castro. Order enhancement and coarsening of self-organized silicon nanodot patterns induced by ion-beam sputtering. Applied Physics Letters. Vol. 89, nº. 23, pp. 233101.1 - 233101.3, Diciembre 2006. [Online: Diciembre 2006]